| Metric | Imperial |
|---|---|
| 1.2m x 10m | 4' x 33' |
| 1.4m x 10m | 4.6' x 33' |
| 1.5m x 10m | 4.92' x 33' |
| Metric | Imperial |
|---|---|
| 1-50mm | 1/32" - 2" |
| TECHNICAL SPECIFICATION | ||||
|---|---|---|---|---|
| PROPERTIES | TEST METHOD | VALUES (FPS UNITS) | TEST METHOD | VALUES (METRIC UNITS) |
| SPECIFIC GRAVITY | ASTM D297 | 0.98 lb/ft³ | DIN 53508 | 1.02 g/cm³ |
| HARDNESS | ASTM D2240 | 40 ± 5 Sh A | DIN 53505 | 40 ± 5 Sh A |
| TENSILE STRENGTH (min) | ASTM D412 | 2100 PSI | DIN 53504 | 150 kg/cm² |
| ELONGATION AT BREAK (min) | ASTM D412 | 600% | DIN 53504 | 600% |
| ABRASION RESISTANCE (max) | ASTM D5963 | 120 mm³ | DIN 53516 | 120 mm³ |
| COMPRESSION SET(70°C/24 hrs/25% set) (max) | ASTM D395 METHOD B | 30% | DIN 53517 | 30% |
| TEAR RESISTANCE (Angular) min | ASTM D624 | 196 lbs/inch | DIN 53515 | 35 kg/cm |
| RESILIENCE | 75% | 75% | ||
| CHANGE IN PROPERTIES | ||||
| HEAT AGING (72 hrs at 70°C) | ASTM D573 | |||
| HARDNESS (Pts) | +5 (max) | +5 (max) | ||
| TENSILE STRENGTH (%) | +10 / -25 | +10 / -25 | ||
| ELONGATION AT BREAK (%) | +10 / -25 | +10 / -25 | ||
| VOLUME SWELL AT 70°C FOR 72 HRS/IN | ASTM D471 | |||
| ASTM OIL NO.1 | NOT RECOMMENDED | NOT RECOMMENDED | ||
| ASTM OIL NO.2 | NOT RECOMMENDED | NOT RECOMMENDED | ||
| ASTM OIL NO.3 | NOT RECOMMENDED | NOT RECOMMENDED | ||
| CHEMICAL RESISTANCE | ||||
| OZONE | ASTM D1149 | FAIR | FAIR | |
| DILUTE ACIDS AND BASES | GOOD | GOOD | ||
| CONCENTRATED ACIDS AND BASES | FAIR | FAIR | ||
| OILS | NOT RECOMMENDED | NOT RECOMMENDED | ||
| SOLVENTS | NOT RECOMMENDED | NOT RECOMMENDED | ||
| TEMPERATURE RANGE | -40° to +80° C | -40° to +80° C | ||
| COLOUR | PINK | PINK | ||